A335 P22

A335 P22 is a kind of chrome moly pipes (ASME S/A335, Chrome-Moly) listed in ASTM A335, which has become a standard in the power generation industry and the petrochemical industry, not only because of its tensile strength, corrosion resistance and high-temperature strength, but also because of its cost-effectiveness.

This slideshow requires JavaScript.

Packing:

Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthly delivery or as requested.

Inspection and Test:

Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength,Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test,No-destructive Test, Hydrostatic Test.

Surface treatment:

Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.

Chemical Compositions(%)
Compositions Data
UNS Designa-tion K21590
Carbon 0.05-0.15
Manganese 0.30-0.60
Phosphorus(max.) 0.025
Sulfur(max.) 0.025
Silicon 0.50-1.00
Nickel
Chromium 1.90-2.60
Molybdenum 0.87-1.13
Other Elements
Mechanical properties for ASTM A335 P22
Properties Data
Tensile strength, min, (MPa) 415 Mpa
Yield strength, min, (MPa) 205 Mpa
Elongation, min, (%), L/T 30/20

(Note: This is summarized information from ASME Specification A335. Please refer to the specific Standard or Specification or contact us for more details.)

Material & Manufacture

Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.

Heat Treatment
  • A / N+T
  • N+T / Q+T
  • N+T
Mechanical Tests Specified
  • Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
  • For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
  • For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test:
  • P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Notes for Bend Test:
  • For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
  • Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
  • The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.
Related products maybe you like
High Temperature service tube
High Temperature Service Pipe
Chrome Moly Tubing
A335 CHROME MOLY PIPE, , &
Astm A335 chrome moly pipe
ASTM A335 P22 pipe