ASTM A182 Standard Specification

A182 / A182M – 12a Standard Specification for Forged or Rolled Alloy and Stainless Steel Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service.

ASTM A182 is a martensitic stainless steel. The additions of Nickel and Molybdenum, which gives it excellent sub zero notch ductility, superior to other standard 13 Cr, 410 and 420 Mod martensitic stainless steels.

UNS S41500 steel is air hardening, with little danger of thick sections cracking during heat treatment.

In addition to limiting the maximum hardness allowed to 23 HRC max, NACE MR0175 imposes heat treatment temperature restrictions.

The weldability and corrosion resistance of ASTM A182 are also excellent, being extensively used in the manufacture of Valve Bodies, Flanges, Seats, Gates, Tubulars, etc.

ASTM A182 specifies a minimum 0.2 PS value of 95 KSI. This NACE approved grade is limited to 75 KSI because of the hardness restriction.

This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

Chemical Requirements of ASTM A182 material (Composition, %, max)
Steel No. Type Chemical composition
C Si S P Mn Cr Ni Mo Other ób ós δ5 HB
F11 CL1 0.05-0.15 0.5-1 0.03 0.03 0.3-0.6 1-1.5 0.44-0.65 415 205 20 121-174 ψ%:45
F11 CL2 0.1-0.2 0.5-1 0.04 0.04 0.3-0.8 1-1.5 0.44-0.65 485 275 20 143-207 ψ%:30
F11 CL3 0.1-0.2 0.5-1 0.04 0.04 0.3-0.8 1-1.5 0.44-0.65 515 310 20 156-207 ψ%:30
F12 CL1 0.05-0.15 0.5 0.045 0.045 0.3-0.6 0.8-1.25 0.44-0.65 415 205 20 121-174 ψ%:45
F12 CL2 0.1-0.2 0.1-0.6 0.04 0.04 0.3-0.8 0.8-1.25 0.44-0.65 485 275 20 143-207 ψ%:30
F304 0.08 1 0.03 0.045 2 18-20 8-11 N:0.1 515 205 30 ψ%:50
F304H 0.04-0.1 1 0.03 0.045 2 18-20 8-11 515 205 30 ψ%:50
F304L 0.035 1 0.03 0.045 2 18-20 8-13 N:0.1 485 170 30 ψ%:50
F316L 0.035 1 0.03 0.045 2 16-18 10-15 2-3 N:0.1 485 170 30 ψ%:50
F317 0.08 1 0.03 0.045 2 18-20 11-15 3-4 515 205 30 ψ%:50
F321 0.08 1 0.03 0.045 2 17-19 9-12 Ti:5C%-0.7 515 205 30 ψ%:50
F347 0.08 1 0.03 0.045 2 17-20 9-13 Ti:10C%-1.1 515 205 30 ψ%:50

Note: composition of Cu, N, V, Co are none or few.

Mechanical Requirements  of ASTM A182 material
Material Symbol Tensile Strength
min, MPa
Yield point
min, Mpa
Elongation
min, %
Reduction of area
min, %
ASTM A182 F304 515 205 30 50
ASTM A182 F304L 485 170 30 50
ASTM A182 F316 515 205 30 50
ASTM A182 F316L 485 170 30 50
ASTM A182 F321 515 205 30 50
Related products maybe you like
ASTM A182 STAINLESS STEEL FLANGES
Pipe Material
What is a Butt Weld (Buttweld) ?
STANDARD CARBON STEEL FLANGES
ANSI/ B16.25, Buttwelding Ends
Piping and
3D BENDS are used are in 10 applications

Leave a Reply

Your email address will not be published. Required fields are marked *